現如今，濟南注塑加工的技術已經相當成熟，從事濟南塑料外殼加工的企業更是越來越多。但是，濟南塑料外殼加工畢竟是一件相當復雜的事，其間還是會出現一些小問題的。下面我們便來簡單介紹下濟南注塑加工的外殼加工表面縮水的原因。Today, Ji'nan injection molding technology has been quite mature, engaged in the processing of plastic shell Tianjin enterprises are more and more. However, the Ji'nan plastic casing processing is a very complex thing, after all, there will be some small problems. Here we will briefly introduce the Ji'nan injection molding processing shell surface shrinkage causes.

濟南注塑加工表面縮水是在塑料外殼的表面發生凹坑狀，一般出現在體積收縮量較大的肉厚部位。塑料外殼在冷卻的過程中，發生體積收縮，由此發生向中心部收縮的拉拽力。Ji'nan injection molding is shrinking surface concave on the surface of the plastic shell, generally appear in the flesh part of large volume shrinkage. During the cooling process, the plastic shell has a volume contraction, and thus the pulling force which is contracted to the center part is generated.

此時受到表面冷料層的剛性和樹脂收縮力之間平衡性的影響，冷料層較弱時，向塑料外殼中心部發生拉拽力，出現在產品表面上表現為凹陷狀。冷料層較強時，塑料外殼的中心部位會產生真空氣泡。At the same time, the effect of the balance between the rigidity of the surface cold material layer and the shrinkage force of the resin is affected, and the pulling force of the central part of the plastic shell is weak when the cold material layer is weak. When the cold material layer is strong, the central part of the plastic shell will produce vacuum bubbles.

濟南注塑加工廠家認為，在肉厚較厚區域，冷料表層的剛性和樹脂收縮力的平衡性與塑料外殼表面的冷卻速度息息相關，冷卻速度較快時形成真空氣泡。相反，較慢時形成縮水。另外，冷卻速度變慢，體積收縮差會變小，縮水狀況也會變小。Ji'nan plastic processing factory, in the thick thick area, the cooling speed and the surface of the plastic shell of the surface of the rigid and cold material balance resin shrinkage force is closely related to the cooling rate of vacuum bubble formation. On the contrary, the slow formation of shrinkage. In addition, the cooling rate is slow, the volume contraction difference will become smaller, shrink situation will become smaller.